5,11,17,23,29,35,41,47-octa-tert-butyl-49,50,51,52,53,54,55,56-octakis-(3-propylsulphonic acid)calix[8]arene

• 分子结构分类: 有机化合物 - 苯类化合物 - 苯酚醚
• 英文名称: 5,11,17,23,29,35,41,47-octa-tert-butyl-49,50,51,52,53,54,55,56-octakis-(3-propylsulphonic acid)calix[8]arene
• 英文别名: 3-[[5,11,17,23,29,35,41,47-Octatert-butyl-50,51,52,53,54,55,56-heptakis(3-sulfopropoxy)-49-nonacyclo[43.3.1.13,7.19,13.115,19.121,25.127,31.133,37.139,43]hexapentaconta-1(48),3,5,7(56),9,11,13(55),15,17,19(54),21,23,25(53),27(52),28,30,33(51),34,36,39(50),40,42,45(49),46-tetracosaenyl]oxy]propane-1-sulfonic acid；3-[[5,11,17,23,29,35,41,47-octatert-butyl-50,51,52,53,54,55,56-heptakis(3-sulfopropoxy)-49-nonacyclo[43.3.1.13,7.19,13.115,19.121,25.127,31.133,37.139,43]hexapentaconta-1(48),3,5,7(56),9,11,13(55),15,17,19(54),21,23,25(53),27(52),28,30,33(51),34,36,39(50),40,42,45(49),46-tetracosaenyl]oxy]propane-1-sulfonic acid
• 化学式: C₁₁₂H₁₆₀O₃₂S₈
• 分子量: 2275.01
• InChiKey: JAZHKHPJEJKFGW-UHFFFAOYSA-N

计算性质

• 辛醇/水分配系数(LogP)：
  22.5
• 重原子数：
  152
• 可旋转键数：
  48
• 环数：
  9.0
• sp3杂化的碳原子比例：
  0.57
• 拓扑面积：
  576
• 氢给体数：
  8
• 氢受体数：
  32

反应信息

• 作为产物：
  描述：

  1,3-丙烷磺内酯 、 4-叔丁基杯[8]芳烃 在 正丁基锂 作用下， 以 二甲基亚砜 为溶剂， 反应 72.0h， 以98%的产率得到5,11,17,23,29,35,41,47-octa-tert-butyl-49,50,51,52,53,54,55,56-octakis-(3-propylsulphonic acid)calix[8]arene
  参考文献：
  名称：

  两种新合成的杯芳烃衍生物在1 M HCl溶液中抑制低碳钢腐蚀的实验研究

  摘要：

  已通过失重和电化学测量（极化和阻抗）研究了两种杯芳烃对摩尔盐酸中低碳钢腐蚀的抑制作用，包括抑制剂浓度和温度的影响。所得结果表明，在存在该化合物的情况下，腐蚀速率显着降低，其中一种化合物在浓度为10 -3  M时的最大抑制率为98.2％。在两种新的杯芳烃浓度不同的情况下，在45–75°C的温度范围内研究了温度对腐蚀行为的影响。化合物的抑制效率随抑制剂浓度的增加而增加，并且与温度无关。极化曲线表明，杯芳烃是混合型抑制剂。碳钢表面对抑制剂的吸附遵循Langmuir吸附等温线。还确定了一些用于溶解和吸附过程的热力学数据。

  DOI：

  10.1007/s11164-012-0869-2

文献信息

• Experimental study of inhibition of corrosion of mild steel in 1 M HCl solution by two newly synthesized calixarene derivatives
  作者：M. Kaddouri、S. Rekkab、M. Bouklah、B. Hammouti、A. Aouniti、Z. Kabouche

  DOI：10.1007/s11164-012-0869-2

  日期：2013.10

  Inhibition of the corrosion of mild steel in molar hydrochloric acid by two calixarenes, including the effect of inhibitor concentration and temperature, has been investigated by use of weight loss and electrochemical measurements (polarisation and impedance). The results obtained showed that the rate of corrosion decreased substantially in the presence of the compounds, with maximum inhibition of

  已通过失重和电化学测量（极化和阻抗）研究了两种杯芳烃对摩尔盐酸中低碳钢腐蚀的抑制作用，包括抑制剂浓度和温度的影响。所得结果表明，在存在该化合物的情况下，腐蚀速率显着降低，其中一种化合物在浓度为10 -3  M时的最大抑制率为98.2％。在两种新的杯芳烃浓度不同的情况下，在45–75°C的温度范围内研究了温度对腐蚀行为的影响。化合物的抑制效率随抑制剂浓度的增加而增加，并且与温度无关。极化曲线表明，杯芳烃是混合型抑制剂。碳钢表面对抑制剂的吸附遵循Langmuir吸附等温线。还确定了一些用于溶解和吸附过程的热力学数据。
• Design, synthesis and anticoagulant activity of new flexible calix[8]arene sulfonic acids
  作者：Seifeddine Rekkab、Mesbah Lahouel、Taibi Ben Hadda、Caroline Félix、Zahia Kabouche

  DOI：10.1016/j.crci.2012.05.024

  日期：2013.7

  Résumés Anglais Français Four new calix[8]arene sulfonic acids (2a-b, 3a-b) were synthesized. The anticoagulant activity and POM virtual screening of these flexible calixarenes have been established. Quatre acides calix[8]arene sulfoniques (2a-b, 3a-b) inédits ont été synthétisés. L’activité anticoagulante et le screening virtuel par la méthode de calcul POM de ces calixarenes flexibles ont été établis.

  摘要 英语 法语 合成了四种新的杯[8]芳烃磺酸(2a-b, 3a-b)。这些柔性杯芳烃的抗凝血活性和 POM 虚拟筛选已经建立。 合成了四种先前未发表的杯[8]芳烃磺酸（2a-b、3a-b）。建立了这些柔性杯芳烃的抗凝血活性和POM计算方法的虚拟筛选。