chromium carbide | 12011-60-8

• 分子结构分类: 有机化合物 - 碳氢化合物衍生物
• 英文名称: chromium carbide
• 英文别名: chromium;methane
• CAS: 12011-60-8
• 化学式: CCr
• 分子量: 64.007
• InChiKey: FAUVSYDAUYVNHI-UHFFFAOYSA-N

计算性质

• 辛醇/水分配系数(LogP)：
  0.63
• 重原子数：
  2
• 可旋转键数：
  0
• 环数：
  0.0
• sp3杂化的碳原子比例：
  1.0
• 拓扑面积：
  0
• 氢给体数：
  0
• 氢受体数：
  0

反应信息

• 作为反应物：
  描述：

  氢化铝 、 chromium carbide 以 neat (no solvent, solid phase) 为溶剂， 生成 chromium aluminum carbide
  参考文献：
  名称：

  Cyclic oxidation of Cr2AlC between 1000 and 1300°C in air

  摘要：

  Fully dense, monolithic ternary Cr2AlC compounds were synthesized via a powder metallurgical route, and their cyclic oxidation behavior was investigated between 1000 and 1300 degrees C in air for up to 100 h. At 1000 and 1100 degrees C, Cr2AlC displayed excellent cyclic oxidation resistance by forming a less than 5 mu m-thick Al2O3 oxide layer and a narrow Cr7C3 underlayer. At 1200 and 1300 degrees C, an outer (Al2O3, Cr2O3)-mixed oxide layer, an intermediate Cr2O3 oxide layer, an inner Al2O3 oxide layer, and a Cr7C3 underlayer formed on the surface. From 1200 degrees C, scale cracking and spalling began to occur locally to a small extent. At 1300 degrees C, the cyclic oxidation resistance deteriorated owing to the formation of voids and the spallation of the scales. (C) 2007 Elsevier B.V. All rights reserved.

  DOI：

  10.1016/j.jallcom.2007.10.018
• 作为产物：
  描述：

  chromium carbide 以 neat (no solvent) 为溶剂， 以0%的产率得到chromium carbide
  参考文献：
  名称：

  Bloom, D. S.; Grant, N. J., Transactions of the American Institute of Mining, Metallurgical and Petroleum Engineers, 1950, vol. 188, p. 41 - 46

  摘要：

  DOI：

文献信息

• MOCVD of hard metallurgical coatings: Examples in the Cr–C–N system
  作者：F. Maury

  DOI：10.1016/j.electacta.2004.10.088

  日期：2005.8

  growth processes are mainly based on the use of bis(benzene)chromium as chromium source and various co-reactives. Then, from a good control of the reactive gas phase, it is possible to combine these MOCVD processes to grow in the same reactor protective coatings designed with a complex architecture based on polyphased, nanostructured or multilayer structure which exhibit enhanced properties. These deposition

  Cr-C-N三元体系的所有单个相，包括稳定相和亚稳态相，都可以通过金属有机化学气相沉积（MOCVD）在低温下沉积。这些生长过程主要基于使用双（苯）铬作为铬源和各种共反应物。然后，通过对反应性气相的良好控制，可以将这些MOCVD工艺组合在一起，在同一反应器保护涂层中生长，该保护涂层的设计基于具有增强性能的多相，纳米结构或多层结构，结构复杂。描述了这些沉积过程，并讨论了涂层的主要特征。
• Chemical composition and structural transformations of amorphous chromium coatings electrodeposited from Cr(III) electrolytes
  作者：Olga V. Safonova、Ludmila N. Vykhodtseva、Nikolai A. Polyakov、Janine C. Swarbrick、Marcin Sikora、Pieter Glatzel、Viktor A. Safonov

  DOI：10.1016/j.electacta.2010.08.108

  日期：2010.12

  Amorphous chromium coatings were electrodeposited from Cr(III)-based solutions containing organic (HCOONa) or phosphorus-containing (NaH2PO2) additives. Their structure was studied by a combination of X-ray diffraction (XRD), valence-to-core X-ray emission spectroscopy (XES) and X-ray absorption spectroscopy (XAS) at the Cr K-edge. Metalloid atoms (C or P) incorporated in electroplates structure are chemically

  从含有机（HCOONa）或含磷（NaH 2 PO 2）的Cr（III）基溶液中电沉积非晶态铬涂层）添加剂。通过在Cr K边缘处结合X射线衍射（XRD），价铁心X射线发射光谱（XES）和X射线吸收光谱（XAS）来研究其结构。结合在电镀结构中的准金属原子（C或P）与铬化学键合（即位于第一配位壳中）。在真空中在升高的温度下退火时，这些无定形涂层结晶成包含金属铬和碳化铬或磷化铬的相的混合物。价核XES数据的定量分析表明，非晶态涂层中铬的平均局部结构在结晶过程中不会发生显着变化。
• Synthesis of metastable chromium carbide nanomaterials and their electrocatalytic activity for the hydrogen evolution reaction
  作者：Samantha M. Schmuecker、Dale Clouser、Theodore J. Kraus、Brian M. Leonard

  DOI：10.1039/c7dt01404j

  日期：——

  Transition metal carbides including chromium, molybdenum, and tungsten are of particular interest as renewable energy catalysts due to their low cost and abundance. While several single metal carbide systems form multiple phases with different compositions and crystal structures, most of these materials are not as well studied due to their limited synthetic approaches and instability. By taking advantage

  包括铬，钼和钨在内的过渡金属碳化物由于其低成本和高含量而作为可再生能源催化剂特别受关注。尽管几种单一的金属碳化物体系形成具有不同组成和晶体结构的多相，但由于合成方法的局限性和不稳定性，大多数此类材料尚未得到很好的研究。通过利用低温盐通量合成方法，这些独特的相可以更容易地合成和分离为相纯物质。例如，碳化铬形成五种不同的晶体结构，包括三个共同相Cr3C2，Cr7C3和Cr23C6，以及两个研究较少的相Cr2C和CrC。所有五种化合物均采用盐通量法合成，并通过X射线衍射（XRD）进行表征，扫描电子显微镜（SEM），X射线光电子能谱（XPS）和析氢反应（HER）的电催化测试。这种低温方法允许常规访问复杂相图中的多种化合物，并以合成方式分离各相。这代表了在合成稀有相（如岩盐CrC和六角形Cr2C）方面迈出的重要一步，并允许对其潜在的催化性能和未来应用进行研究。
• Preparation of nano-scale Cr3C2 particles dispersed on alumina particles by MOCVD in fluidized reactor and carbothermal treatment
  作者：Hao-Tung Lin、Jow-Lay Huang、Sheng-Chang Wang、Chen-Fu Lin

  DOI：10.1016/j.jallcom.2005.07.071

  日期：2006.6

  Nano-scale Cr 3 C 2 powder with an average particle size of 50–80 nm, uniformly coated on alumina particles, has been prepared by metal organic chemical vapor deposition (MOCVD) in the fluidized chamber, using the pyrolysis of Cr(CO) 6 precursor, and carbothermal treatment in the CH 4 and H 2 gas mixtures. The Cr(CO) 6 precursor was characterized by differential scanning calorimetry (DSC) to understand

  摘要 利用金属有机化学气相沉积 (MOCVD) 在流化室中利用 Cr(CO) 热解制备了平均粒径为 50-80 nm 的纳米级 Cr 3 C 2 粉末，均匀包覆在氧化铝颗粒上。 ) 6 前驱体，并在 CH 4 和 H 2 气体混合物中进行碳热处理。Cr(CO) 6 前驱体通过差示扫描量热法 (DSC) 进行表征，以了解前驱体的分解温度，确定为 163 °C。当在流化床中在 300 和 400°C 下热解时，前驱体分解并在 Al 2 O 3 颗粒表面形成 CrC 1 - x 、Cr 2 O 3 和游离碳的混合物。通过配备能量色散光谱仪 (EDS) 的 X 射线衍射仪 (XRD) 和透射电子显微镜 (TEM) 检查所得粉末，用于研究相组成和微观结构。在流化室中在 300 和 400 °C 下制造的沉积态颗粒分别是非晶态和结晶态。TG/DTA 研究的热行为表明无定形粉末在约 400 °C 的 DTA
• Mechanically driven syntheses of carbides and silcides
  作者：G. Le Caër、E. Bauer-Grosse、A. Pianelli、E. Bouzy、P. Matteazzi

  DOI：10.1007/bf01129932

  日期：1990.11