N,N-diphenyl-4-[1-phenyl-2-[4-[4-[2-phenyl-2-[4-(N-phenylanilino)phenyl]ethenyl]phenyl]phenyl]ethenyl]aniline | 1384440-14-5

• 分子结构分类: 有机化合物 - 有机氮化合物
• 英文名称: N,N-diphenyl-4-[1-phenyl-2-[4-[4-[2-phenyl-2-[4-(N-phenylanilino)phenyl]ethenyl]phenyl]phenyl]ethenyl]aniline
• CAS: 1384440-14-5
• 化学式: C₆₄H₄₈N₂
• 分子量: 845.099
• InChiKey: AUMOKDUJKTZORF-UHFFFAOYSA-N

计算性质

• 辛醇/水分配系数(LogP)：
  18.3
• 重原子数：
  66
• 可旋转键数：
  13
• 环数：
  10.0
• sp3杂化的碳原子比例：
  0.0
• 拓扑面积：
  6.5
• 氢给体数：
  0
• 氢受体数：
  2

反应信息

• 作为产物：
  描述：

  4,4'-双(二乙氧基膦酰甲基)联苯 、 (4-(diphenylamino)phenyl)(phenyl)methanone 在 potassium tert-butylate 作用下， 以 四氢呋喃 为溶剂， 以72%的产率得到N,N-diphenyl-4-[1-phenyl-2-[4-[4-[2-phenyl-2-[4-(N-phenylanilino)phenyl]ethenyl]phenyl]phenyl]ethenyl]aniline
  参考文献：
  名称：

  Highly Efficient Blue Light-Emitting Materials Based on Arylamine Substituted DPVBi Derivatives

  摘要：

  通过 Horner-Wadsworth-Emmons 反应合成了一系列芳基胺取代的 DPVBi 衍生物（1-4）。通过制造具有以下结构的多层 OLED 器件，考察了它们的电致发光特性：ITO/DNTPD（40 nm）/NPB（20 nm）/掺杂了 MADN（20 nm）/Alq3（40 nm）/Liq（1.0 nm）/Al 的 2% DPVBi 衍生物 (1-4)。所有器件都显示出高效的蓝色发射。特别是，利用化合物 1 作为发射层的掺杂剂，制造出了高效率的蓝色 OLED。使用化合物 1 作为掺杂剂的蓝色 OLED 的最大亮度、发光效率、功率效率和 CIE 坐标分别为：10 V 时 16110 cd/m2，20 mA/cm2 时 10.1 cd/A，20 mA/cm2 时 4.37 lm/W，8 V 时 (x = 0.197, y = 0.358)。此外，使用化合物 4 作为掺杂剂的器件显示出高效的深蓝色发射，其亮度、发光效率、功率效率和 CIE 坐标分别为：10 V 时 7005 cd/m2、20 mA/cm2 时 6.25 cd/A、20 mA/cm2 时 2.50 lm/W 和 8 V 时 (x = 0.151, y = 0.143)。

  DOI：

  10.1166/jnn.2011.4798

文献信息

• Highly Efficient Blue Light-Emitting Materials Based on Arylamine Substituted DPVBi Derivatives
  作者：Suhyun Oh、Kum Hee Lee、Ji Hyun Seo、Young Kwan Kim、Seung Soo Yoon

  DOI：10.1166/jnn.2011.4798

  日期：2011.8.1

  A series of arylamine substituted DPVBi derivatives (1–4) were synthesized via the Horner-Wadsworth-Emmons reaction. Their electroluminescent properties were examined by fabricating a multilayer OLED device with the following structure: ITO/DNTPD (40 nm)/NPB (20 nm)/2% DPVBi derivatives (1–4) doped in MADN (20 nm)/Alq3 (40 nm)/Liq (1.0 nm)/Al. All devices showed efficient blue emission. In particular, a high efficiency blue OLED was fabricated using compound 1 as a dopant in the emitting layer. The maximum luminance, luminous efficiency, power efficiency and CIE coordinates of the blue OLED using compound 1 as a dopant were 16110 cd/m2 at 10 V, 10.1 cd/A at 20 mA/cm2, 4.37 lm/W at 20 mA/cm2, and (x = 0.197, y = 0.358) at 8 V, respectively. Moreover, a device using compound 4 as the dopant exhibited efficient deep blue emission with a luminance, luminous efficiency, power efficiency and CIE coordinates of 7005 cd/m2 at 10 V, 6.25 cd/A at 20 mA/cm2, 2.50 lm/W at 20 mA/cm2 and (x = 0.151, y = 0.143) at 8 V, respectively.

  通过 Horner-Wadsworth-Emmons 反应合成了一系列芳基胺取代的 DPVBi 衍生物（1-4）。通过制造具有以下结构的多层 OLED 器件，考察了它们的电致发光特性：ITO/DNTPD（40 nm）/NPB（20 nm）/掺杂了 MADN（20 nm）/Alq3（40 nm）/Liq（1.0 nm）/Al 的 2% DPVBi 衍生物 (1-4)。所有器件都显示出高效的蓝色发射。特别是，利用化合物 1 作为发射层的掺杂剂，制造出了高效率的蓝色 OLED。使用化合物 1 作为掺杂剂的蓝色 OLED 的最大亮度、发光效率、功率效率和 CIE 坐标分别为：10 V 时 16110 cd/m2，20 mA/cm2 时 10.1 cd/A，20 mA/cm2 时 4.37 lm/W，8 V 时 (x = 0.197, y = 0.358)。此外，使用化合物 4 作为掺杂剂的器件显示出高效的深蓝色发射，其亮度、发光效率、功率效率和 CIE 坐标分别为：10 V 时 7005 cd/m2、20 mA/cm2 时 6.25 cd/A、20 mA/cm2 时 2.50 lm/W 和 8 V 时 (x = 0.151, y = 0.143)。