octa[(5,6-epoxyhexyl)dimethylsilyloxy]silsesquioxane

• 分子结构分类: 有机化合物 - 有机金属化合物 - 有机类金属化合物
• 英文名称: octa[(5,6-epoxyhexyl)dimethylsilyloxy]silsesquioxane
• 英文别名: [3,5,7,9,11,13,15-Heptakis[[dimethyl-[4-(oxiran-2-yl)butyl]silyl]oxy]-2,4,6,8,10,12,14,16,17,18,19,20-dodecaoxa-1,3,5,7,9,11,13,15-octasilapentacyclo[9.5.1.13,9.15,15.17,13]icosan-1-yl]oxy-dimethyl-[4-(oxiran-2-yl)butyl]silane；[3,5,7,9,11,13,15-heptakis[[dimethyl-[4-(oxiran-2-yl)butyl]silyl]oxy]-2,4,6,8,10,12,14,16,17,18,19,20-dodecaoxa-1,3,5,7,9,11,13,15-octasilapentacyclo[9.5.1.13,9.15,15.17,13]icosan-1-yl]oxy-dimethyl-[4-(oxiran-2-yl)butyl]silane
• 化学式: C₆₄H₁₃₆O₂₈Si₁₆
• 分子量: 1803.14
• InChiKey: MHCPJCRGHWFLBP-UHFFFAOYSA-N

计算性质

• 辛醇/水分配系数(LogP)：
  14.06
• 重原子数：
  108
• 可旋转键数：
  56
• 环数：
  14.0
• sp3杂化的碳原子比例：
  1.0
• 拓扑面积：
  285
• 氢给体数：
  0
• 氢受体数：
  28

反应信息

• 作为产物：
  描述：

  1,2-环氧基-5-己烯 、 octakis(dimethylsiloxy)octasilsesquioxane 在 platinum divinyltetramethyldisiloxane 作用下， 以 甲苯 为溶剂， 反应 24.0h， 以90%的产率得到octa[(5,6-epoxyhexyl)dimethylsilyloxy]silsesquioxane
  参考文献：
  名称：

  Thermomechanical properties of polyimide-epoxy nanocomposites from cubic silsesquioxane epoxides

  摘要：

  新型聚酰亚胺-环氧有机-无机纳米复合材料是通过聚酰胺酸大分子与两种POSS环氧化物——八[(环氧环己基乙基)二甲基硅氧基]倍半硅氧烷(OC)和八[(环氧己基)二甲基硅氧基]倍半硅氧烷(OH)的原位固化制备的。 OC和OH的两个系列纳米复合材料之间的比较提供了通过调整POSS分子的纳米系链结构来控制宏观尺度性能的典型例子。 DMA 研究得出结论，聚酰亚胺-环氧纳米复合材料的交联密度显着增加；纳米复合材料网络主要由聚酰亚胺分子的末端胺基和POSS分子的环氧基团之间的连接形成。此外，有趣的是，尽管纳米复合材料的交联密度显着增加，但压缩模量、硬度和热膨胀系数仅略有变化。

  DOI：

  10.1039/b405427j

文献信息

• Thermomechanical properties of polyimide-epoxy nanocomposites from cubic silsesquioxane epoxides
  作者：Junchao Huang、Yang Xiao、Khine Yi Mya、Xueming Liu、Chaobin He、Jie Dai、Yeen Ping Siow

  DOI：10.1039/b405427j

  日期：——

  Novel polyimide-epoxy organic–inorganic nanocomposites are prepared by in situ curing of polyamic acid macromolecules with two POSS epoxides, octa[(epoxycyclohexylethyl)dimethylsilyloxy]silsesquioxane (OC) and octa[(epoxyhexyl)dimethylsilyloxy]silsesquioxane (OH). Comparison between two series of nanocomposites from OC and OH provides a typical example of controlling the macro-scale properties by adjusting the nano-tether structure of the POSS molecules. DMA studies conclude that the crosslink densities of the polyimide-epoxy nanocomposites increase significantly; the nanocomposite networks are predominantly formed by the linkage between the terminal amine groups of the polyimide molecules and the epoxide groups of the POSS molecules. Furthermore, it is interesting to observe that although the crosslink densities of nanocomposites increase significantly, the compressive moduli, hardness and coefficients of thermal expansion change only slightly.

  新型聚酰亚胺-环氧有机-无机纳米复合材料是通过聚酰胺酸大分子与两种POSS环氧化物——八[(环氧环己基乙基)二甲基硅氧基]倍半硅氧烷(OC)和八[(环氧己基)二甲基硅氧基]倍半硅氧烷(OH)的原位固化制备的。 OC和OH的两个系列纳米复合材料之间的比较提供了通过调整POSS分子的纳米系链结构来控制宏观尺度性能的典型例子。 DMA 研究得出结论，聚酰亚胺-环氧纳米复合材料的交联密度显着增加；纳米复合材料网络主要由聚酰亚胺分子的末端胺基和POSS分子的环氧基团之间的连接形成。此外，有趣的是，尽管纳米复合材料的交联密度显着增加，但压缩模量、硬度和热膨胀系数仅略有变化。